PA66 CFRT UD tapes (also named CFRT uni-directional tapes) offer exceptional performance in the most demanding environments. Its excellent properties include chemical resistance, low moisture absorption, high melting point and high crystallization rate.

This kind of unidirectional tape possesses the highest mechanical properties among UD tapes made by various CFRT materials (continuous fiber reinforced thermoplastic composites). Its tensile strength can reach 700 Mpa and its flexural strength is up to 800 Mpa.



Properties Test Standards Condition Units Typical Value
Fiberglass Content ISO3451-1:2008 23℃ Wt% 60
Density ISO1183-1:2012 23℃ g/cm3 1.72
Tape Thickness / 23℃ mm 0.32
Tensile Strength ISO527-5Tape 5mm/min MPa 700
Flexural Strength ISO14125 2mm/min MPa 800
Flexural Modulus ISO14125 2mm/min GPa 34

Note1: Colored product performance may be different from the above values.

Note2: Typical values are the average laboratory data, when used only for reference , not as a products standard.

Note2: Above conditions only reference, according to different equipment, different molds and product requirements, process must be appropriately adjusted.



Automotive and sporting goods.

Besides PA66, we have PA 6 CFRT UD tapes for alternatives, which is a little thinner with higher tensile and flexural strength. You can also find other CFRT products in TOPOLO such as PP UD tapes, PPS UD tapes, thermoplastic composite sheets and honeycomb sandwich panels. TOPOLO is dedicated to the research and design of new composite materials for lightweight solutions of automobile. Our products of continuous fiber reinforced thermoplastic composites are ideal choices for your economical and high quality requirements.